Gamma irradiation induced surface modification of (PVC/HDPE)/ZnO nanocomposite for enhancing the oil removal and conductivity using COMSOL multiphysics
HomeHome > News > Gamma irradiation induced surface modification of (PVC/HDPE)/ZnO nanocomposite for enhancing the oil removal and conductivity using COMSOL multiphysics

Gamma irradiation induced surface modification of (PVC/HDPE)/ZnO nanocomposite for enhancing the oil removal and conductivity using COMSOL multiphysics

May 26, 2023

Scientific Reports volume 13, Article number: 7514 (2023) Cite this article

417 Accesses

Metrics details

Blend nanocomposite film was prepared by loadings of irradiated ZnO in ratios of (5 wt%) inside the PVC/HDPE matrix using a hot-melt extruder technique. The physical and chemical properties of the irradiated and unirradiated ZnO samples are compared. The Vis–UV spectrum of ZnO shows an absorption peak at a wavelength of 373 nm that was slightly red-shifted to 375 nm for an irradiated sample of ZnO at a dose of 25 kGy due to the defect of crystal structure by the oxygen vacancy during gamma irradiations. This growth of the defect site leads to a decrease in energy gaps from 3.8 to 2.08 eV. AC conductivity of ZnO sample increased after the gamma irradiation process (25 kGy). The (PVC/HDPE)/ZnO nanocomposites were re-irradiated with γ rays at 25 kGy in the presence of four different media (silicon oil, sodium silicate, paraffin wax and water). FTIR and XRD were performed to monitor the changes in chemical composition. The new peak at 1723 cm−1 attributed to C=O groups was observed in irradiated (PVC/HDPE)ZnO samples at only sodium silicate and water media. This process induced new function groups on the surface of the (PVC/HDPE)/ZnO blend sample. This work aims to develop (PVC/HDPE)ZnO for oil/water separation. The highest oil adsorption capability was observed in samples functionalized by C=O groups based on the different tested oils. The results suggest that the surface characterization of the (PVC/HDPE)/ZnO can be modified to enhance the oil adsorption potential. Further, the gamma irradiation dose significantly enhanced the AC conductivity compared to the unirradiated sample. According to COMSOL Multiphysics, the irradiated sample (PVC/HDPE)ZnO in water shows perfect uniform electric field distribution in medium voltage cables (22.000 V).

The production of polymers with specified physical–chemical properties combined with the features granted by surface modifications has become possible through the fascinating and practical surface modification of polymeric materials1,2,3,4. There are various ways to change the properties of polymers, including blending, grafting, and curing. The physical blending of two (or more) polymers results in the desired characteristics. In the process known as "grafting", monomers are covalently attached (modified) to the polymer chain. In contrast, an oligomer mixture is polymerized during curing to generate a coating physically attached to the substrate. Grafting is a promising approach for adding unique functional groups to polymers to change their original properties and expand the range of their applications5,6.

After the irradiation process some atoms and groups such as hydrogen atoms and carbon-hydrogen groups are released from polymers, there is a considerable shift in the stoichiometry of the polymer. If present in the polymer chains, other atomic species (O, F, Cl, N, etc.) are also expelled7,8,9. It is well known that after radiation exposure, polymers lose hydrogen, which has the effect of physical polymer properties. Chain scission produces smaller units and oligomer chain, a profusion of double bonds, and the emergence of radicals. These small carbon-enriched particles may aggregate into electrically conductive clusters due to their electrostatic attraction9.

Polymer blends physiochemical characteristics and electric conductivity can be improved by adding nanofillers like ZnO nanoparticles in various ratios10,11,12,13,14. Parangusan et al.15 studied the piezoelectric properties of electrospun nanofibers made from neat polyvinylidene fluoride hexafluoropropylene (PVDF-HFP) and PVDF-HFP/Co-ZnO. It was observed that the tidy PVDF-HFP and PVDF-HFP/2 wt% Co-ZnO nanofibers have dielectric constants of 8 and 38, respectively. These results suggest that the reported nanocomposite can create flexible, wearable, self-powered electrical systems. Thermoplastic polymers such as high-density polyethylene (HDPE) nanocomposite can be reinforced with graphite nanoplatelets, nanodiamonds and carbon nanotube to improvise rheological, thermal and mechanical properties16,17,18,19. PVC surface modification in the past is carried out using plasma, corona discharge, chemical grafting, electric discharge, metal vapor deposition (MVD), flame treatment or direct chemical modification (oxidation, hydrolysis, etc.), and even some physical modification of the surface. This study aims to increase PVC hydrophilicity in (PVC/HDPE)ZnO that has been irradiated with Ɣ-rays on various media, including water, paraffin wax, silicon oil, and sodium silicate solutions. Gamma irradiation has several advantages over other techniques, including high penetration power, quick processing, uniform-dose distribution, system flexibility, and ability to be used in various environments20,21,22,23,24,25. Gamma irradiation is an eco-friendly method and the most productive26,27,28,29,30,31. This study also aims to increase the hydrophilicity of (PVC/HDPE) for oil/water separation applications. Applications for oil–water separation are crucial for industrial processes like those involving petroleum, metalworking, ship bilge water, and the food industry, which uses fats, oils, and grease, among other things.

Oil/water separation is a crucial subject of study for scientific research and concerns the environment, the economy, and society. On the one hand, the most prevalent pollution in the world today is oily wastewater produced by industries like steel, aluminium, food, textile, leather, petrochemical, and metal finishing. On the other hand, frequent oil leak accidents are extremely concerning because the discharge can cause significant energy loss and catastrophic environmental degradation. Additionally, since even a small amount of fuel oil could jeopardise transportation safety, expelling water from fuel oil is essential in the vehicle, ship, and aviation industries. In response to these enormous obstacles, scientists have consistently focused on creating new methods and materials for oil/water separation. Many common separation technologies are used today, including gravity separation, centrifugation, ultrasonic separation, air flotation, electric field, coagulation, and biological treatment. These methods can handle most separation requirements by carefully integrating physical, chemical, and biological techniques. Due to its superhydrophobicity, high surface area, chemical inertness, low density, recyclability, and selectivity, carbon nanotubes based on membranes have been developed for oil spill clean-ups by Parangusan et al.32. The addition of carbon nanotube greatly improves the electrical conductivity of polymer composites with a sudden transition from an insulator to a semiconductor due to the decrease of tunneling distance33,34,35.

Preparing highly dispersed polymer-based nanocomposites made of PVC/HDPE embedded with ZnO nanoparticle using gamma irradiation is one of the primary objectives of the current study. Investigations have been done on how gamma radiation affects the physiochemical characteristics of ZnO nanoparticles. To meet the emergency response needs of effective oil spill separation, it was also examined how to increase the hydrophobicity of blended surfaces by irradiating samples at various media (water, paraffin wax, silicon oil, and sodium silicate solutions). The novelty of current research is the developed nanocomposite blend of (PVC/conductivity HDPE)/ZnO properties for acting as dual functions as oil removal and uniform the electric field distribution in medium voltage cables by surface modification.

polyvinyl chloride (PVC) was supplied from Misrelhegaz company, Egypt and high-density polyethylene (HDPE) was supplied from Sabic company, Saudi Arabia with technical data out line in Table 1 from the market and used without further purification. Chemicals such as sodium silicate solutions (Na2OxSiO2) M.W 184–254, paraffin wax (CnH2n+2 melting point: 50–57 °C) and silicon oil (Xiameter PMX-200 Silicone) were supplied from the market and used as it is.

Polyvinyl chloride was melt-mixed with HDPE in the ratio (30/70) wt/wt% using a twin screw extruder (CTW100P; Haake Poly lab Rheomix, Germany). The content of ZnO was 5wt% and adding in the meld blends of PVC and HDPE and the rotating screw speed in the extruder was 120 rpm. The extrudates obtained from the twin screw extruder were two-roll milled (Lab Tech Engineering Co., Bangkok, Thailand) at 170 °C for 7 min before compression-molding with a hot press (Lab Tech Engineering Co., Bangkok, Thailand) at 170 °C with a pressure of 150 kg/cm2 for 4 min. The moulded (PVC/HDPE)/ZnO composite was cut into test pieces for further experimental evaluation.

A typical experiment created ZnO nanoparticles using the traditional sol–gel process. The solution, A of zing salt, was created by dissolving 20.196 g (0.10 mol) of zinc acetate in 600 mL of water/ethanol in a ratio 80/20 v/v% and stirring it for 60 min at room temperature. A solution of 0.20 mol of oxalic acid dehydrates was obtained by dissolving 2.520 g in 800 mL of water/ethanol in ratio 80/20 v/v% and stirred at a temperature of 50 °C for 60 min to create Solution B. Warm solution A was constantly mixed for one hour while solution B was added dropwise. A white sol was obtained, aged to create a gel, and then dried for 24 h at 100 °C. ZnO was finally produced using thermal processing at calcination temperatures of 600 °C for 3 h.

Another advantage of radiation-induced surface modification in four different media (silicon oil, sodium silicate paraffin wax and water) is that it enables tailored modifications ranging from surface to bulk of backbone polymers, unlike photo- and plasma initiation, which imparts surface modification only. The modification process can improve the hydrophilicity or hydrophobicity of (PVC/HDPE)/ZnO samples or their conductivity or modify its oil adsorption. Sheets of irradiated (PVC/HDPE)/ZnO samples are cut into strip samples and re-irradiated with γ rays at 25 kGy in four different media (silicon oil, sodium silicate paraffin wax and water). The irradiation process is carried out under ambient conditions and a dose rate of 0.67 kGy/h is maintained by using a Co-60 source (Irradiation is performed NCRR, AEAE).

An ultraviolet (UV)-visible spectrophotometer (Ultraviolet-3600, Schimadzu) was used to monitor the characterization of the band gab of synthesized ZnO and irradiated ZnO at a scanning range of 200–500 nm. The Fourier-transform infrared spectroscopy (FTIR/ATR) (ATR–FTIR) Vertex 70, Bruker Optik GmbH, Ettlingen, Germany is a technique used to obtain the chemical change structure of surface modified (PVC/HDPE)/ZnO nanocomposite. The powder X-ray diffraction (XRD) technique used the XRD-7000 (Schimadzu, Germany). The process for the crystalline analysis of the ZnO with Cukα radiation (λ = 1.5418 Å). The mechanical properties and tensile characteristics in the dumbbells shape of obtained modified (PVC/HDPE)ZnO samples were measured using an Intron mechanical testing machine under ASTM D638 (model 5569). The surface morphology of (PVC/HDPE)ZnO sample was examined using a Scanning Electron Microscope (SEM) of ZEISS EVO 15 SEM, UK. The contact angle of of synthesized ZnO and irradiated ZnO was measured on a horizontal surface by a KRÜSS EasyDrop DSA20 instrument. AC conductivity σAC(ω) was measured by LCR bridge model Hioki 3532 which was used to measure the impedance Z and the phase angle between the applied AC voltage and the resulting current in the samples of sample (PVC/HDPE)/ZnO and surface modified (PVC/HDPE)/ZnO. The frequency ranged from 0.00 to 500 Hz. The variation in AC conductivity with a frequency at ambient temperature on (ln-ln) scale. The impedance Z, sample capacitance Cp, and loss tangent Tanδ were measured using a programmable automatic 3532 LCR meter. The resistance R was parallel to all capacitance values Cp was taken from the bridge's screen. The module of COMSOL multiphysics software of V5.2 in distribution systems is used underground medium voltage cable (XLPE). The working layer in the analysis test is copper conductor with 3.5 mm radius, inner semiconductor 4.5 mm, XLPE insulation 10.5 mm and outer semiconductor 11.25 mm. All radii have been estimated from the middle of the conductor of copper. The physics properties: AC/DC copper using finite element method, mesh processing: Finer and computer RAM: 8 GB. The relative tolerance in the solution processing in COMSOL software is 2.147 for (PVC/HDPE)/ZnO at 0 kGy and 2.22 at 25 kGy.

The optical properties of nanoparticles powder of two samples of unirradiated and irradiated ZnO at dose of 25 kGy were represented in Fig. 1. The Vis–UV spectrum shows characteristic absorption peaks of ZnO (0 kGy) at the wavelength of 242 nm, 271 nm and 373 nm which can be attributed to the intrinsic band-gap absorption of ZnO–NPs because of the electron transitions from the valence band to the conduction band (O2 → Zn3d)36, The absorption spectrum of ZnO–NPs also suggested the narrow nano size particle distribution. The band gap energy of ZnO NPs can be estimated according to the formula

where plank's constant (h) is (6.626 × 10−34 J s), the velocity of light (c) is (3 × 108 m s−1) and λ (373 nm) is the wavelength. The band gap energy of ZnO NPs was calculated as 3.8 eV.

The optical properties of unirradiated and irradiated ZnO NPs at dose of (a) 0 kGy and (b) 25 kGy.

After an irradiation dose of 25 kGy, the characteristic absorption peak of the ZnO NPs at wavelength of 373 nm was slightly red-shifted relative to the absorption maximum of 375 nm. It may be due to the defect of crystal structure by the oxygen vacancy during gamma irradiations. This growth of the defect site leads to a decrease in energy gaps to become 2.08 from 3.8 eV with an irradiation dose of 25 kGy. The development of the defect state could be caused by the reduction of compressive stress in the ZnO films. The reduced compressive stress of irradiated ZnO may be attributed to the well-aligned ZnO hexagonal nanoparticles37.

Figure 2 shows the XRD analysis of un-irradiated and irradiated ZnO nanoparticles at 25 kGy. The XRD curve shows 7 intensity peaks located at 2θ = 31.57°, 34.13°, 36.00°, 47.57°, 56.45°, 62.72° and 67.70°, confirming the hexagonal wurtzite structure of ZnO NPs according to38. After gamma irradiation the 2θ of 31.57°, 34.13°, 36.00° were shifted to 31.66°, 34.31°, 36.15°. Also the d-spacing was decreased from (2.831, 2.617, 2.489) Å to (2.823, 2.611 and 2.482) Å, respectively. The decrease of d-spacing after gamma irradiation is expected due to metal oxide defect and atom displacement phenomena39,40.

The XRD analysis of un-irradiated and irradiated ZnO nanoparticles at dose of 25 kGy.

The effect of gamma irradiation at dose of 25 kGy on the contact angles of ZnO was investigated. Figure 3 shows the wettability character of un-irradiated and irradiated ZnO nanoparticles by measuring the contact angles of the water drop. The contact angle of the irradiated sample is increased from 54.36° to 65.25° compared to the blank sample. The increased contact angle of the irradiated sample is due to the increased ZnO orientation and the well-aligned ZnO hexagonal nanoparticles, as confirmed by band gab data analysis and XRD data analysis.

Show the contact angle of un-irradiated and irradiated ZnO nanoparticles at dose of 25 kGy.

Figure 4 shows the variation in AC conductivity as a function of ln frequency at two irradiation doses (0 to 25) kGy for ZnO nanoparticles. It is observed that the two samples exhibit different AC conductivity phases with different values over the whole range of measured frequency. The Ac conductivity of the irradiated sample is higher than unirradiated samples. The possible increase in defects on ZnO's crystal structure and the expansion of conduction routes between ZnO particles are linked to the growth in AC conductivity. The bulk conductivity may rise due to more charge carriers being able to "jump" by tunneling, and it also rises with gamma irradiation exposed41,42. Table 2 outline the main change in the physiochemical properties of irradiated and unirradiated ZnO sample.

Shows the electric AC conductivity of un-irradiated and irradiated ZnO nanoparticles at 25 kGy.

SEM images of 5% ZnO and PVC/HDPE mixture are shown in Fig. 5a. It is quite clear that the addition of ZnO nanocomposite caused the surface of the sample to appear rougher. This is useful in increasing oil adsorption on the sample's surface. The same result agreed with the results obtained by Dai et al., Haq et al. and Barroso-Solares et al. Dai et al.43 found that the surface roughness of poly(lactic acid) (PLA) fibers can be controlled by increasing the content of Zn2+ in metal framework of (ZIF-8). Oil adsorption is accelerating due to the higher roughness of (PLA/ZIF-8) fiber surface. Haq et al.44 prepared oil adsorbent resin system includes (unsaturated polyester + epoxidized soybean oil + nanoclay) with varying nanoclay amounts. He and coauthor obviously that the surface's roughness is increased due to the addition of nanoclay. Barroso-Solares et al.45 prepared mixed nano fibers of two polymers, poly(methyl methacrylate) (PMMA) and polycaprolactone (PCL), with weight ratios of 70/30, 50/50 and 30/70 incorporated with 1 wt% of silicon oxide fumed nanoparticles. It was noted that the 50/50 PMMA/PCL sample shows the most promising compromise between the oil absorption capacity, oil selectivity, and mechanical properties, this is due to the increased roughness of the 50/50 PMMA/PCL fibers respect to the other two samples (70/30 and 30/70). Figure 5b shows better evidence regarding the distribution of ZnO nanoparticles obtained via elemental EDX mapping of Zn and O as the main elements from ZnO and of C and Cl from (PVC/HDPE) blend in the case of (PVC/HDPE) ZnO nanocomposites. These two elements of (Zn and O) are present in the surface in well distribution identified in PVC/HDPE matrix. EDX / mapping analysis did not provide evidence of any other trace elements.

SEM (a) and EDX/mapping (b) of (PVC/HDPE)ZnO nanocomposite.

The obtained compatible blends of (PVC/HDPE) ZnO irradiated at different media (paraffin wax, silicon oil, sodium silicate and water) as an efficient method for the hydrophobicity modification of the surface of blends to use in oil/water separation. Surface modification is modifying the surface of (PVC/HDPE) ZnO blends by bringing chemical and physical properties different from the blank sample. The physicochemical properties of surface-modified (PVC/HDPE) ZnO blends were performed using other characteristics such as FTIR, mechanical properties and XRD. The chemical structure of the surface modification of (PVC/HDPE)ZnO blend films using FTIR spectroscopy is shown in Fig. 6. The two FTIR peaks located at 2918 cm−1 and 623 cm−1 are characteristic peaks of C–H and C–Cl bonds of PVC molecules, respectively. The peak at 1290 cm−1 is attributed to trans CH3 in polyethylene molecules46. The peak at 1723 cm−1 attributed to C=O groups was observed in unirradiated (PVC/HDPE)ZnO samples and irradiated samples at sodium silicate and water media. On the other hand, the C=O groups completely disappeared in case (PVC/HDPE) ZnO samples were irradiated in paraffin wax and silicon oil. The peak intensity of 1290 cm−1 was increased in the case of the irradiated sample at silicon oil and sodium silicate media due to the formation of Si-CH3 at 1250 cm−147,48,49.

The FTIR spectra of PVC/HDPE (a) unirradiated, (b) irradiated 25 kGy, (c) in paraffin wax, (d) in silicon oil, (e) in sodium silicate and (f) in water.

Figure 7 shows the X-ray diffraction (XRD) patterns of the blank and the modified surface of irradiated (PVC/HDPE) at the dose of 25 kGy. It is noted that, the XRD peaks of ZnO is not clear in Fig. 7a,b samples of (PVC/HDPE) at the dose of 0 kGy and 25 kGy, respectively due to the surface modification of (PVC/HDPE)/ZnO leading to concentration the nanoparticles in the surface of plastic sheet similar to the bulk of the samples in Fig. 7c–f. The characteristic XRD peaks of HDPE are located at ~ 21° and 23°, which correspond to the typical semi-crystalline nature of orthorhombic unit cells of (110) and (200) reflection planes, respectively50,51,52. Figure 7 confirms plane (110)'s diffraction peaks are almost changing in all modified (PVC/HDPE) samples. This means the modified surface is placed on the plane (110) of HDPE53. Also, Fig. 7 shows a very broad XRD peak of PVC ranging from 14° to 24°; this indicates that PVC is amorphous54. Also, XRD in Fig. 7 represents the XRD pattern for ZnO nanoparticles located at 2∂ = 31.45°, 34.22°, 35.96°, 42.42°, 47.31°, 56.26°, 62.72°, 67.70°, 67.84°, 68.96° and 72.45° correspond to reflections from the crystal planes 100, 002, 101, 102, 110, 103, 200, 112, 201, 004 and 202 This ensures the formation of the ZnO in a pure hexagonal wurtzite phase38.

The XRD spectra (a) unirradiated, (b) irradiated (25 kGy), (c) in paraffin wax, (d) silicon oil, (e) sodium silicate and (f) water of (PVC/HDPE)ZnO blends.

From the bar graph Fig. 8, it can be perceived that the force (N), elongation (mm) and Young's modules (MPa) of unirradiated (PVC/HDPE)ZnO blends are much more than all irradiated (PVC/HDPE)ZnO blends samples. The Young's modulus and force of blank (PVC/HDPE)ZnO (0 kGy) and at (25 kGy) were 51.7 MPa, 193.66 N and 24.22 MPa, 104.3 N, respectively. After gamma irradiation, Young's modulus and force were observed to be decreased due to the defect state of the atomic bonds in blends induced by gamma irradiation. On the other hand, Young's modulus and force were observed to be decreased in all treated samples after surface treatment. These results justify that the surface modification contributed to changes in the surface's chemical structure; falls in mechanical properties can be due to the low interfacial bonding between the bulk and surface of the blend chain. The intense interfacial bonding between the bulk and surface of the treated blend chain may cause an elongation increase compared to blank samples. Further, the mechanical properties of the (PVC/HDPE)ZnO blend gamma irradiation treated in Na–Si exhibit higher Young's modulus and force value than other treated (PVC/HDPE)ZnO blend samples. This may be attributed to a harder physical bonding effect and the formation of weak bonds on the (PVC/HDPE)ZnO blends surface.

Comparison of mechanical properties regarding Force, Elongation and Young's modulus.

Oils absorb on surfaces due to a surface phenomenon. As a result, adsorbents have vast surface areas, most of which are interior surfaces that enclose the massive pores and capillaries of highly porous materials. As shown in Fig. 9 the oil-adsorbed power of (PVC/HDPE)/ZnO is decreased after irradiation. One of the most reasons is the porous adsorbents become smaller and reduce their capability for efficiently adsorbing due to gamma irradiation-induced cross-linked reactions. While after surface modification, the four modified (PVC/HDPE)/ZnO show a wide spectrum of adsorption capability for the six different kinds of oils. The performance characteristics of adsorbents largely relate to their intraparticle properties such as surface chemical compositions and surface hydrophobicity. The hydrophobic surface area of modified samples and the functionalised distribution of groups concerning pore size and roughness surface generally are primary determinants of adsorption capacity.

The adsorption capacity of six different modified irradiated (PVC/HDPE)ZnO composites for removal of six kinds of oils.

On the other hand, the density of removal oil and API number (American Petroleum Institute number is used to identify the oil and gas wells) should be considered. The effect of API on the adsorption potential of oil was in inverse relations ship. As show in Fig. 9 the percentage adsorption capacity of oils was observed to increase in direct proportion with a decrease in API value and at an inverse proportionality with low functionalized sites in modified (PVC/HDPE)ZnO samples due to the presence of functional groups found in crude oils55. According to previous literature, crude oils have other groups containing –C=C–, C=O and OH with excess sulfur and nitrogen56. For castor oil, the adsorbent sample of (PVC/HDPE)/ZnO irradiated at a 25 kGy in water media increased from 73 to 157% compared to the blank sample irradiated at 25 kGy. As depicted in Fig. 9, the adsorption uptake was observed to be changed depending on the kind of adsorbent. As the functionalized sites on the surface were increased from irradiated samples at 25 kGy in water and NaSi solutions, the adsorption uptake of oil increased consistently. The adsorption uptake of motor oil increased from 26%, 56%, 64%, 73% and 75% for modified irradiated samples in air, wax, Si oil, water and NaSi. The highest adsorption capability of oils was observed in samples functionalized by C=O groups. The availability of the functional group sites on the adsorbed surface enhanced the oil removal capability. The results suggest that the surface characterization of the (PVC/HDPE)/ZnO can be modified to enhance the oil adsorption potential.

Figure 10 shows the AC conductivity of (PVC/HDPE)/ZnO, which varied in the same behavior independently on the surface modification and the type of function group formation. However, it should be noted that each sample's percolation threshold depends on the gamma irradiation condition in different solutions. Figure 10 shows the lowest conductivity of un-irradiated samples of (PVC/HDPE)/ZnO seemed to increase twice after irradiation at a 25 kGy. This is due to the gamma irradiation-induced defect by atom displacement that increased the electron transition after the formation of holes. Additionally, dehydrochlorination of PVC molecules brought on by gamma irradiation may result in the formation of conjugated double bonds. Throughout these conjugations, the electrons then become mobile. Consequently, electron mobility contributes to the material's overall conductivity57,58.

The AC conductivity of surface modified (PVC/HDPE)/ZnO.

On the other hand, the two irradiated samples of (PVC/HDPE)/ZnO in water and NaSi solutions had higher conductivity values for the same given frequency. This is due to forming new function groups in the modified surface detected by FTIR data. The functional groups can serve as a host matrix for electron transition.

To simulate the distribution of the electric field in MV cables, utilise COMSOL Multiphysics. The distribution of the electric fields inside the (PVC/HDPE)ZnO unirradiated sample is depicted in Fig. 11. The electric field distribution inside the sample is not uniform at 1 mm of arc length. The electric field distribution for irradiation (PVC/HDPE)ZnO/water is becoming uniform and steadily declines from the interior to the outside, as shown in Fig. 12. This is due to the new C=O function groups ability to maintain an even electrical field while lowering electrostatic tension.

Electric field distribution in medium-voltage of unirradiated (PVC/HDPE)ZnO.

Electric field distribution in medium-voltage cables of irradiated (PVC/HDPE)ZnO water.

ZnO was irradiated at dose of 25 kGy for improved it physiochemical properties, The Vis–UV spectrum of ZnO shows an absorption peak at a wavelength of 373 nm that was slightly red-shifted to 375 nm for an irradiated sample of ZnO at a dose of 25 kGy due to the defect of crystal structure by the oxygen vacancy during gamma irradiations.

This growth of the defect site leads to a decrease in energy gaps from 3.8 to become 2.08 eV.

The contact angle of the irradiated sample is increased from 54.36° to 65.25° compared to the blank sample.

Surface modification of the (PVC/HDPE)ZnO with gamma irradiation treatment was investigated.

The gamma irradiation process at dose of 25 kGy was performance in four different media such as (paraffin wax, Si oil, NaSi and water) to improve the surface by a functionalized group of PVC/HDPE)ZnO samples.

FTIR spectra revealed chemical change on the (PVC/HDPE)ZnO surface after gamma irradiation treatment in water and NaSi.

The C=O peaks appeared in the expected FTIR, confirming the sample surface's alteration.

The surface of the (PVC/HDPE)ZnO sample enhances its oil removal capability compared to blank samples.

The adsorption uptake of motor oil increased from 26%, 56%, 64%, 73% and 75% for modified irradiated samples in air, wax, Si oil, water and NaSi.

The highest adsorption capability of oils was observed in samples functionalized by C=O groups.

According to COMSOL Multiphysics, the irradiated (PVC/HDPE)ZnO sample in water shows uniform electric field distribution in medium voltage cable (22.000 v).

The future work of surface modified (PVC/HDPE)ZnO sample can be expanded the use of (PVC/HDPE)ZnO based on their AC conductivity that was an enhancement.

The data that support the findings of this study are available from the corresponding author upon reasonable request.

Sánchez, L. D., Brack, N., Postma, A., Pigram, P. J. & Meagher, L. Surface modification of electrospun fibres for biomedical applications: A focus on radical polymerization methods. Biomaterials 106, 24–45 (2016).

Article Google Scholar

Amani, H. et al. Controlling cell behavior through the design of biomaterial surfaces: A focus on surface modification techniques. Adv. Mater. Interfaces 6, 1900572 (2019).

Article Google Scholar

Bangar, S. P. et al. Surface modifications of cellulose nanocrystals: Processes, properties, and applications. Food Hydrocolloids 130, 107689 (2022).

Article CAS Google Scholar

Goswami, A., Pillai, S. C. & McGranaghan, G. Surface modifications to enhance dropwise condensation. Surf. Interfaces 25, 101143 (2021).

Article CAS Google Scholar

Das, S., Dey, R., Hasnain, M. S. & Nayak, A. K. Graft copolymers of polysaccharides: Synthesis techniques and pharmaceutical applications. In Tailor-Made Polysaccharides in Drug Delivery 129–156 (2023).

Hernández-Arriaga, A. M., Campano, C., Rivero-Buceta, V. & Prieto, M. A. When microbial biotechnology meets material engineering. Microb. Biotechnol. 15, 149–163 (2022).

Article PubMed Google Scholar

Krstić, J. et al. Improvement of antibacterial activity of Ag-poly (vinyl-alcohol)/chitosan hydrogel by optimizing the procedure of radiolytic synthesis. Radiat. Phys. Chem. 194, 110045 (2022).

Article Google Scholar

Madani, M. et al. Green synthesis of nanoparticles for varied applications: Green renewable resources and energy-efficient synthetic routes. Nanotechnol. Rev. 11, 731–759 (2022).

Article CAS Google Scholar

Tareen, A. K. et al. Recent advances in novel graphene: New horizons in renewable energy storage technologies. J. Mater. Chem. C 10, 11472–11531 (2022).

Article CAS Google Scholar

Parangusan, H., Ponnamma, D., Al-Maadeed, M. A. A. & Marimuthu, A. Nanoflower-like yttrium-doped ZnO photocatalyst for the degradation of methylene blue dye. Photochem. Photobiol. 94, 237–246 (2018).

Article CAS PubMed Google Scholar

Ponnamma, D., Elgawady, Y., Nair, S. S., Hassan, M. K. & Al-Maadeed, M. A. A. Core-shell nanofibers of polyvinyl alcohol/polylactic acid containing TiO2 nanotubes for natural sunlight driven photocatalysis. Macromol. Mater. Eng. 307, 2100482 (2022).

Article CAS Google Scholar

AlAhzm, A. M., Alejli, M. O., Ponnamma, D., Elgawady, Y. & Al-Maadeed, M. A. A. Piezoelectric properties of zinc oxide/iron oxide filled polyvinylidene fluoride nanocomposite fibers. J. Mater. Sci. Mater. Electron. 32, 14610–14622 (2021).

Article CAS Google Scholar

Sharshir, A. I. et al. Experimental investigation of E-beam effect on the electric field distribution in cross-linked polyethylene/ZnO nanocomposites for medium-voltage cables simulated by COMSOL multiphysics. J. Anal. Sci. Technol. 13, 1–13 (2022).

Article Google Scholar

Sharshir, A. I. et al. Simulating the electric field distribution in medium-voltage cables of cross-linked polyethylene/Cu nanocomposites irradiated by E-beam with reference to the XLPE market. Plast. Rubber Compos. 51, 281–292 (2022).

Article ADS CAS Google Scholar

Parangusan, H., Ponnamma, D. & Al-Maadeed, M. A. A. Stretchable electrospun PVDF-HFP/Co-ZnO nanofibers as piezoelectric nanogenerators. Sci. Rep. 8, 1–11 (2018).

Article CAS Google Scholar

Amirapu, S. L., Nelapati, G. S., Yalamanchili, H., Badgayan, N. D. & Sahu, S. K. HDPE based polymeric nanodiamond nanocomposite for total knee arthoplasty: A finite element based approach. Mater. Today Proc. 56, 1622–1628 (2022).

Article Google Scholar

Sahu, S. K. & Sreekanth, P. S. R. Artificial neural network for prediction of mechanical properties of HDPE based nanodiamond nanocomposite. 폴리머 46, 614–620 (2022).

Sahu, S. K. & Rama Sreekanth, P. S. Multiscale RVE modeling for assessing effective elastic modulus of HDPE based polymer matrix nanocomposite reinforced with nanodiamond. Int. J. Interact. Des. Manuf. 1, 1–10 (2022).

Google Scholar

Sahu, S. K. & Rama Sreekanth, P. S. Mechanical, thermal and rheological properties of thermoplastic polymer nanocomposite reinforced with nanodiamond, carbon nanotube and graphite nanoplatelets. Adv. Mater. Process. Technol. 8, 2086–2096 (2022).

Google Scholar

Elhady, M., Ghobashy, M. & Mahmoud, M. A. Effect of gamma irradiation on the adhesive property and antibacterial activity of blend polymer (abietic acid-EVA). Polymer Polymer Compos. 29, 138–147 (2021).

Article CAS Google Scholar

El-Wahab, A. et al. Radiation synthesis of poly vinylpyrrolidone and polyacrylamide hydrogels as soil conditioner. Al-Azhar Bull. Sci. 29, 1–7 (2018).

Article Google Scholar

Ghobashy, M. M. Ionizing Radiation Effects and Applications Vol. 113 (InTech Rijeka, 2018).

Google Scholar

Ghobashy, M. M. et al. Radiation crosslinking of modifying super absorbent (polyacrylamide/gelatin) hydrogel as fertilizers carrier and soil conditioner. J. Polym. Environ. 26, 3981–3994 (2018).

Article CAS Google Scholar

Ghobashy, M. M. & Elhady, M. Radiation crosslinked magnetized wax (PE/Fe3O4) nano composite for selective oil adsorption. Compos. Commun. 3, 18–22 (2017).

Article Google Scholar

Ghobashy, M. M. & El-Sattar, N. E. A. Radiation synthesis of rapidly self-healing hydrogel derived from poly (acrylic acid) with good mechanical strength. Macromol. Chem. Phys. 221, 2000218 (2020).

Article CAS Google Scholar

Ghobashy, M. M. et al. Controlling radiation degradation of a CMC solution to optimize the swelling of acrylic acid hydrogel as water and fertilizer carriers. Polym. Adv. Technol. 32, 514–524 (2021).

Article CAS Google Scholar

Ghobashy, M. M. & Khafaga, M. R. Chemical modification of nano polyacrylonitrile prepared by emulsion polymerization induced by gamma radiation and their use for removal of some metal ions. J. Polym. Environ. 25, 343–348 (2017).

Article CAS Google Scholar

Ghobashy, M. M., Reheem, A. M. A. & Mazied, N. A. Ion etching induced surface patterns of blend polymer (poly ethylene glycol–poly methyl methacrylate) irradiated with gamma rays. Int. Polym. Proc. 32, 174–182 (2017).

Article CAS Google Scholar

Younis, S. A., Ghobashy, M. M., Bassioni, G. & Gupta, A. K. Tailored functionalized polymer nanoparticles using gamma radiation for selected adsorption of barium and strontium in oilfield wastewater. Arab. J. Chem. 13, 3762–3774 (2020).

Article CAS Google Scholar

Ghobashy, M. M. et al. Improvement of in vitro dissolution of the poor water-soluble amlodipine drug by solid dispersion with irradiated polyvinylpyrrolidone. ACS Omega 5, 21476–21487 (2020).

Article CAS PubMed PubMed Central Google Scholar

Ghobashy, M. M. & Elhady, M. A. Radiation crosslinked magnetized wax (PE/Fe3O4) nano composite for selective oil adsorption. Compos. Commun. 3, 18–22 (2017).

Article Google Scholar

Parangusan, H., Ponnamma, D., Hassan, M. K., Adham, S. & Al-Maadeed, M. A. A. Designing carbon nanotube-based oil absorbing membranes from gamma irradiated and electrospun polystyrene nanocomposites. Materials 12, 709 (2019).

Article ADS CAS PubMed PubMed Central Google Scholar

Veiskarami, A., Sardari, D., Malekie, S., Mofrad, F. B. & Kashian, S. Computational prediction of electrical percolation threshold in polymer/graphene-based nanocomposites with finite element method. J. Polym. Eng. 42, 936–945 (2022).

Article CAS Google Scholar

Malekie, S. & Ziaie, F. A two-dimensional simulation to predict the electrical behavior of carbon nanotube/polymer composites. J. Polym. Eng. 37, 205–210 (2017).

Article CAS Google Scholar

Eberl, T. Accelerators, spectrometers, detectors and associated. Nucl. Instrum. Methods Phys. Res. A 502, 306–333 (2003).

ADS Google Scholar

Rauf, M. A. et al. Biomimetically synthesized ZnO nanoparticles attain potent antibacterial activity against less susceptible S. aureus skin infection in experimental animals. RSC Adv. 7, 36361–36373 (2017).

Article ADS CAS Google Scholar

Zhao, M. et al. Influence of water content in mixed solvent on surface morphology, wettability, and photoconductivity of ZnO thin films. Nanoscale Res. Lett. 9, 1–8 (2014).

Article ADS Google Scholar

Dar, R. A. et al. Performance of graphene-zinc oxide nanocomposite coated-glassy carbon electrode in the sensitive determination of para-nitrophenol. Sci. Rep. 12, 117 (2022).

Article ADS PubMed PubMed Central Google Scholar

Lee, G. et al. Influence of radiation-induced displacement defect in 1.2 kV SiC metal-oxide-semiconductor field-effect transistors. Micromachines 13, 901 (2022).

Article PubMed PubMed Central Google Scholar

Ubizskii, S. B. et al. Displacement defect formation in complex oxide crystals under irradiation. Phys. Status Solidi A 177, 349–366 (2000).

3.0.CO;2-B" data-track-action="article reference" href="https://doi.org/10.1002%2F%28SICI%291521-396X%28200002%29177%3A2%3C349%3A%3AAID-PSSA349%3E3.0.CO%3B2-B" aria-label="Article reference 40" data-doi="10.1002/(SICI)1521-396X(200002)177:23.0.CO;2-B">Article ADS CAS Google Scholar

Sudha, A., Sharma, S. L. & Gupta, A. N. Achieving sensitive and stable indium oxide thin films for gamma radiation monitoring. Sens. Actuators A 285, 378–385 (2019).

Article CAS Google Scholar

Arshak, K. & Korostynska, O. Response of metal oxide thin film structures to radiation. Mater. Sci. Eng. B 133, 1–7 (2006).

Article CAS Google Scholar

Dai, X., Cao, Y., Shi, X. & Wang, X. The PLA/ZIF-8 nanocomposite membranes: The diameter and surface roughness adjustment by ZIF-8 nanoparticles, high wettability, improved mechanical property, and efficient oil/water separation. Adv. Mater. Interfaces 3, 1600725 (2016).

Article Google Scholar

Haq, M., Burgueño, R., Mohanty, A. K. & Misra, M. Hybrid bio-based composites from blends of unsaturated polyester and soybean oil reinforced with nanoclay and natural fibers. Compos. Sci. Technol. 68, 3344–3351 (2008).

Article CAS Google Scholar

Barroso-Solares, S., Pinto, J., Nanni, G., Fragouli, D. & Athanassiou, A. Enhanced oil removal from water in oil stable emulsions using electrospun nanocomposite fiber mats. RSC Adv. 8, 7641–7650 (2018).

Article ADS CAS PubMed PubMed Central Google Scholar

Furukawa, T. et al. Molecular structure, crystallinity and morphology of polyethylene/polypropylene blends studied by Raman mapping, scanning electron microscopy, wide angle X-ray diffraction, and differential scanning calorimetry. Polym. J. 38, 1127–1136 (2006).

Article CAS Google Scholar

Othman, A. M., Ghobashy, M. M., El-Sattar, A. & Nour, E. A. Radiation synthesis of porous calcium silicate aerogel derived from polyacrylamide hydrogel as thermal insulator. J. Sol-Gel. Sci. Technol. 98, 593–604 (2021).

Article CAS Google Scholar

Oh, T. & Choi, C. K. Comparison between SiOC thin films fabricated by using plasma enhance chemical vapor deposition and SiO2 thin films by using fourier transform infrared spectroscopy. J. Korean Phys. Soc 56, 1150–1155 (2010).

Article CAS Google Scholar

Kim, M. T. Deposition behavior of hexamethydisiloxane films based on the FTIR analysis of Si–O–Si and Si–CH3 bonds. Thin Solid Films 311, 157–163 (1997).

Article ADS CAS Google Scholar

Moradkhani, R., Hosseini-Dastgerdi, Z. & Sirousazar, M. High-density polyethylene/asphaltene composites: Thermal, mechanical and morphological properties. Polym. Polym. Compos. 29, 1528–1533 (2021).

CAS Google Scholar

Nabiyev, A. A. et al. 1 edn 012011 (IOP Publishing).

Benabid, F. Z., Kharchi, N., Zouai, F., Mourad, A.-H.I. & Benachour, D. Impact of co-mixing technique and surface modification of ZnO nanoparticles using stearic acid on their dispersion into HDPE to produce HDPE/ZnO nanocomposites. Polym. Polym. Compos. 27, 389–399 (2019).

CAS Google Scholar

Kaczmarek, H. et al. Influence of glass beads filler and orientation process on piezoelectric properties of polyethylene composites. J. Mater. Sci.: Mater. Electron. 30, 21032–21047 (2019).

CAS Google Scholar

Behboudi, A., Jafarzadeh, Y. & Yegani, R. Polyvinyl chloride/polycarbonate blend ultrafiltration membranes for water treatment. J. Membr. Sci. 534, 18–24 (2017).

Article CAS Google Scholar

Shittu, T. D., Aransiola, E. F. & Alabi-Babalola, O. D. Adsorption performance of modified sponge gourd for crude oil removal. J. Environ. Prot. 11, 65 (2020).

Article CAS Google Scholar

Samanta, A., Ojha, K. & Mandal, A. Interactions between acidic crude oil and alkali and their effects on enhanced oil recovery. Energy Fuels 25, 1642–1649 (2011).

Article CAS Google Scholar

Kemari, Y., Mekhaldi, A., Teguar, M. & Teyssedre, G. 1–4.

Coltro, L., Pitta, J. B. & Madaleno, E. Performance evaluation of new plasticizers for stretch PVC films. Polym. Test. 32, 272–278 (2013).

Article CAS Google Scholar

Download references

Open access funding provided by The Science, Technology & Innovation Funding Authority (STDF) in cooperation with The Egyptian Knowledge Bank (EKB). This work is funded by the Science, Technology & Innovation Funding Authority (STDF) in Project Number 46339.

Radiation Research of Polymer Chemistry Department, National Center for Radiation Research and Technology (NCRRT), Egyptian Atomic Energy Authority (EAEA), Cairo, Egypt

Mohamed Mohamady Ghobashy & Ahmed M. Elbarbary

Faculty of Engineering, Zagazig University, Zagazig, Egypt

Amal. F. Abd El-Gawad, M. A. Farahat & M. I. Ismail

Solid State and Accelerator Department, National Center for Radiation Research and Technology (NCRRT), Egyptian Atomic Energy Authority (EAEA), Cairo, Egypt

S. A. Fayek & A. I. Sharshir

Faculty of Computers and Informatics, University Zagazig, Zagazig, Egypt

Amal. F. Abd El-Gawad

Faculty of Engineering, Egypt University of Informatics, Cairo, Egypt

M. I. Ismail

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

All authors contributed substantially to the conception and design of the work and to the analysis and interpretation of the data. All authors contributed to revisions and approved the final draft. All authors agree to be accountable for all aspects of the work in ensuring that any questions related to the accuracy or integrity of any part of the work are appropriately investigated and resolved. Specific individual contributions in addition to the above: A.I.S. led the drafting of the paper and contributed to data extraction. S.A.F. contributed to literature searching and data extraction. A.F.A.E.-G. contributed to literature searching and drafting sections of the manuscript. M.A.F and M. I. I. contributed to data extraction, data wrote and preparation of figures and tables. A.M.E. contributed to FTIR mesurement. M.M.G. contributed to resolving data extraction outcomes and the Introduction and data wrote. The lead author (A.I.S., the manuscript's guarantor) affirms that the manuscript is an honest, accurate and transparent account of the study being reported. No important aspects of the study have been omitted; and that any discrepancies from the study as planned (and, if relevant, registered) have been explained.

Correspondence to A. I. Sharshir.

The authors declare no competing interests.

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.

Reprints and Permissions

Ghobashy, M.M., F. Abd El-Gawad, A., A. Fayek, S. et al. Gamma irradiation induced surface modification of (PVC/HDPE)/ZnO nanocomposite for enhancing the oil removal and conductivity using COMSOL multiphysics. Sci Rep 13, 7514 (2023). https://doi.org/10.1038/s41598-023-34583-0

Download citation

Received: 04 November 2022

Accepted: 03 May 2023

Published: 09 May 2023

DOI: https://doi.org/10.1038/s41598-023-34583-0

Anyone you share the following link with will be able to read this content:

Sorry, a shareable link is not currently available for this article.

Provided by the Springer Nature SharedIt content-sharing initiative